用于发泡成型的聚丙烯改性研究

第21卷第3期  2006年9月 《天津科技大学学报》 Journal of Tianjin University of Science& Technology

邬素华  (天津科技大学材料科学与化学工程学院，天津300457)

摘要：选用低密度聚乙烯和聚异丁烯作为改性剂，用Brabender熔融共混的方式对聚丙烯(PP)挤出发泡进行了系统的研究，分析了发泡PP配方中各种成分及挤出x-'E条件对发泡材料密度、表观质量及性能的影响。结果表明：PP／LDPE共混体系的发泡倍率较高，发泡片材表面光滑，气孔细密，具有较好的综合性能。

关键词：聚丙烯，泡沫塑料，共混，低密度聚乙烯，聚异丁烯

中图分类号：TQ334．9 文献标识码：A 文章编号：1672-6510(2006)03-0027-04

M odification Research on Polypropylene Foaming Material

W U Su．hua  (College of Material Science and Chemical Engineering，Tianjin University of Science&Technology，Tianjin 300457，China)

Abstract：Extruded polypropylene(PP)foam with LDPE and polyisobutylene were studied systematically by melt blending with brabender．Efects of various ingredients in the formulation and extrusion conditions on density，appearance and properties of~amed polypropylene were analysed．The resuhs showed that PP／LDPE has hi【gh—ratio of foaming ，the surface of foam ed sheet was smooth and has good overall properties．

Keywords：polypropylene；foamed plastics；blending；LDPE；polyisobutylene

泡沫塑料主要品种有聚氨酯(PU)、聚苯乙烯(PS)和聚烯烃(PO)三大类。然而，Ps发泡制品在成型过程中使用的氟氯碳化物会破坏大气臭氧层，其制品废弃物由于体积大、不腐烂、难回收，对周围环境造成“白色污染”，联合国环保组织已决定到2005年全世界范围内停止生产和使用发泡Ps。Pu泡沫片材在发泡过程中存在对人体有害的异氰酸酯残留物，且发泡材料无法回收利用。于是，人们积极地寻求能取代发泡PS、PU的无氟、无毒、轻量化的环境适应性的材料，如采用发泡聚丙烯(PP)。聚丙烯(PP)发泡材料具有优良的耐热性(最高使用温度达130℃)、绝缘性、保温性、耐寒性、耐油性、耐化学药品性、阻隔性以及可降解回收性，尤其适合作为包括食品在内的各种环保包装材料 。但是市面上出售的通用PP由于在发泡温度下表现出熔体强度的骤降，难以将气体保持在树脂中形成泡孔，因此PP发泡材料的生产技术难度很大。

本文针对PP的分子结构特点，通过PP与其他聚合物共混的方法拓宽其熔程，以改善其发泡成型性 。