聚丙烯增韧改性研究

《现代塑料加工应用》 2 0 0 6年第1 8卷第4期  MODERN PI ASTICS PR()CESSING AND APPI ICATIONS

范吉昌 李莹莹  (洛阳工业高等专科学校材料系，河南洛阳，471003)

摘要：

主要研究了聚烯烃热塑性弹性体(POE)在聚丙烯改性中的应用，并与三元乙丙橡胶、二元乙丙橡胶弹性体进行对比，探讨了POE含量对聚丙烯的力学性能的影响。结果表明，POE改性聚丙烯时，质量分数15 的加入量就能起到明显的增韧效果；POE对聚丙烯缺口冲击强度提高较大，而弯曲模量及拉伸强度降低较小。

关键词： 聚丙烯 聚烯烃弹性体 二元乙丙橡胶 三元乙丙橡胶 增韧 改性

Study on Toughening Modification of PoIypropylene

Fan Jichang Li Yingying  (Dept．of Material Sci．and Eng．，Luoyang College of Technology，Louyang，Henan，471003)

Abstract：The application of polyolefin elastomer in polypropylene modification was studied． Compared with elastomers such as ethylene／propylene terpolymer and ethylene／propylene rubber，the influence of the contents of polyolefin elastomer on the mechanical properties of polypropylene was discussed．The results show that 15 polyolefin elastomer has good effects on the toughening of  Polypropylene． Notch impact strength of polypropylene toughened by polyolefin elastomer has a large improvement，and tensile strength and flexural modulus decrease．

Key words：polypropylene；polyolefin elastomer；ethylene／propylene rubber；ethylenepropylene terpolymer；toughening；modification

前 言

聚丙烯(PP)密度小、刚性和硬度高，原料来源广泛，易于加工成型，产品综合性能优良，用途非常广泛，已成为通用树脂中发展最快的品种之一。但是PP也存在一些不足之处，最大的缺点是耐寒性差、低温易脆断；其次是收缩率大、抗蠕变性差、制品尺寸稳定性差、容易产生翘曲变形l1一。为此，出现了一系列的PP／三元乙丙橡胶(EPDM)等改性专用料。最近美国Dow 公司生产的聚烯烃热塑性弹性体[(乙烯／辛烯)共聚
物](POE)比EPDM、二元乙丙橡胶(EPR)在改性PP时更具有性能、价格方面的优势，特别是对PP的增韧效果更为显著|2]。

国内较多以PP／EPDM 体系为生产汽车专用料，且技术比较成熟，而用PP／POE体系生产汽车专用料的还较少，笔者以EPR，EPDM 和POE为增韧剂，分别对PP进行了改性试验，并对3者的增韧效果作了比较分析。